Fabrication of FETs

ABSTRACT

A method of fabricating FETs to reduce parasitics. Contact is made to the source and drain regions through a polycrystalline silicon runner which is aligned with the edge of the gate electrode. This is accomplished by providing a layer such as palladium over the gate electrode and depositing the polycrystalline silicon layer over the device. The polycrystalline silicon and palladium form a silicide which is then selectively etched leaving the remaining polycrystalline silicon aligned with the gate.

BACKGROUND OF THE INVENTION

This invention relates to the fabrication of integrated circuits and in particular to a fabrication sequence for field effect transistors which permits reduced parasitics in the final devices.

With the continuing trend of greater numbers of components in integrated circuits and the need for high speed operation, increasing demands are made on field effect transistors. In particular, as channel lengths become shorter and junctions become shallower, increasing attention must be paid to the device parasitics to insure optimum performance of the transistors. For example, the source and drain junction capacitances and the series resistances between the channel and the contacts to the source and drain regions can significantly affect performance in short channel FETs. Also, when FETs are used as memory cells in dynamic random access memories, the output of a cell will depend inversely on the capacitance of the bit line. Consequently, a reduction in the bit line capacitance, which is the sum of the junction capacitances associated with that bit line, will significantly increase the speed of the memory. Junction capacitances can be reduced by decreasing the area of the source and drain regions. However, this also creates problems in aligning the contacts to these regions. Decreasing source and drain junction depths also increase the series resistance between the source and drain contacts and the channel. This resistance can be reduced by better alignment of the contacts so that they extend close to the channel region.

Other proposals for fabricating FETs have included deposition of a metal such as Pt onto the surfaces of the source and drain regions utilizing a gate electrode as a mask. The metal is then reacted with the exposed silicon to form metal silicide contacts and gates which are self-aligned. Unreacted metal over the silicon oxide (masking) areas is etched away without affecting the silicide. External contact is then provided by an aluminum metalization deposited onto a patterned insulating layer which includes openings over the source, drain and gate silicide regions (see, e.g., U.S. Pat. No. 4,319,395 issued to Lund et al and U.S. Pat. No. 4,343,082 issued to Lepselter et al). Although such techniques are adequate to reduce series resistance, they do not lend themselves easily to reductions in the area of source and drain regions since the openings in the insulating layer for external contact must be aligned within the source and drain areas. Further, direct contact of the silicide regions by the aluminum metal over the source and drain regions can result in spiking, which is a shorting of the junction caused by reaction of aluminum with the underlying silicon substrate. This problem is particularly acute for shallow junctions. In addition, for CMOS devices, where the metal layer must contact both n⁺ and p⁺ junction areas, there are additional constraints in that the metal should not affect the ohmic contact to either conductivity type regions.

Reduced source and drain areas will also aid in reducing the possibility of latchup in CMOS circuits. That is, increased separation is permitted between the adjacent edges of the n⁺ emitter in the p-type tub and the p⁺ emitter in the n-type tub without changing the layout area. Alternatively, smaller source and drain areas permit the layout area to be reduced while maintaining the separation of the adjacent edges of the same n⁺ and p⁺ emitters.

It is therefore a primary object of the invention to provide a method of producing small area, low capacitance source and drain regions with a means of contacting such regions so that the contacts are self-aligned with the gate electrode. It is a further object of the invention to provide contacts to the source and drain regions whih do not lead to spiking.

SUMMARY OF THE INVENTION

These and other objects of the invention are achieved in accordance with the invention which is a method of fabricating a field effect transistor including a source and drain region formed in the surface of a semiconductor substrate with a channel region therebetween. Formed over the channel region is a patterned multi-level electrode structure including successive layers of a gate electrode metal, a first insulator, and a silicide forming metal. A second insulator is formed along the edges of the electrode structure. A layer of polycrystalline silicon is deposited over essentially the entire transistor area and the silicide forming metal is reacted with the polycrystalline silicon so as to form a metal silicide over the electrode structure. The metal silicide is then selectively etched without affecting the first or second insulator or the remaining polycrystalline silicon layer.

BRIEF DESCRIPTION OF THE DRAWING

These and other features of the invention are delineated in detail in the following description. In the drawing:

FIGS. 1-11 are views of a field effect transistor during various stages of fabrication in accordance with one embodiment of the invention.

It will be appreciated that, for purpose of illustration, these figures are not necessarily drawn to scale.

DETAILED DESCRIPTION

FIGS. 1-11 illustrate various stages in the fabrication of a field effect transistor in accordance with one embodiment of the invention. It will be appreciated that the device shown is meant to illustrate only part of an integrated circuit which includes many other components.

As shown in FIG. 1, the processing begins with a silicon-substrate, 10, which in this example is p-conductivity type, upon which is formed by standard techniques an insulating layer, 11, of SiO₂. The layer includes a thin portion, 13, formed over the area of the semiconductor which will comprise the transistor (typically referred to as the gate oxide) and a thick portion, 12, (the field oxide) which serves to mask the areas outside the transistor and to provide electrical isolation. The thin portions are typically 200 Å thick and the thick portions are typically 4000 Å thick. One of the advantages of the invention is the fact that the dimension, t, of the transistor area in the direction of current conduction (covered by 13) can be made small, i.e., typically less than 2 μm. That is, the dimension, t, of the region covered by 13 needs to be only large enough to contain the gate structure (14, 15, 16, 17, of FIG. 2) and provide allowance for a worst case alignment error between the gate and region 12.

As illustrated in FIG. 2, a multi-level electrode structure is formed by standard deposition and photolithography over the area of the semiconductor which will comprise the channel region of the transistor. The structure comprises successive layers of a gate electrode metal, 14, such as polycrystalline silicon, an insulating layer 15, such as SiO₂, and a silicide forming metal layer, 16, which in this example is palladium. Layer, 14, may, alternatively, comprise a composite layer of silicide, such as TaSi₂, on polycrystalline silicon. Formed on the metal layer, 16, is another insulating layer, 17, such as SiO₂ or Si₃ N₄, which may be desirable to protect the metal, 16, from subsequent processing. FIG. 3 shows the same device in a cross-sectional view which is orthogonal to that of FIG. 2 in order to illustrate the fact that part of the electrode structure is formed over the steps between field oxide and gate oxide regions. Typical thicknesses are: 4000 Å for layer 14; 2000 Å for layer 15; 2000 Å for layer 16; and 2000 Å for layer 17. The electrode structure in this example measures approximately 1 μm laterally in FIG. 2 by approximately 1 μm high.

Next, as shown in FIGS. 4 and 5 (the latter being a view orthogonal to that of FIG. 4), an insulating layer, 18, is formed on the edges of the electrode structure to offset the final gate structure from the contacts to be formed later. Several methods are available for forming this offset insulator. In this example, a layer of SiO₂ (not shown) is deposited over the entire structure to a thickness of approximately 1000 Å and is then etched anisotropically as by reactive ion etching. The etch is continued until the layer, 16, is exposed and also the portions of the gate oxide not covered by either the electrode structure or the vertical portions (18) of the SiO₂ layer are removed. The vertical portions (18) of the etched oxide remain due to the anisotropy of the etch. Layer 17 may be removed as part of the reactive ion etch (if, e.g., it is SiO₂) or in a separate wet etch (if, e.g., it is Si₃ N₄). (It will be appreciated that sidewall oxide will also be formed on the walls of layer, 12, in FIG. 4 and subsequent figures thus slightly narrowing the original dimension t (by typically 0.1μ on each edge). This sidewall oxide is normally the same material as the initial oxide, 12, and is not shown in the figures.)

As shown in FIG. 6, a doped polycrystalline layer, 19, is then formed over essentially the entire structure. The layer may be doped either in situ during a chemical vapor deposition or by a later implant of the dopant. In this example, the layer is doped with arsenic (As) and deposited to a thickness of approximately 2000 Å by standard chemical vapor deposition at a temperature of approximately 600 degrees C. During such a reaction, the exposed Pd layer will react with the polycrystalline silicon to form a PdSi layer, 20.

This silicide layer can be selectively etched without etching the remainder of the polycrystalline silicon layer, 19, or the SiO₂ layers, 15 and 18, as illustrated in FIG. 7 and in the orthogonal view of the same stage illustrated in FIG. 8. This can be accomplished, for example, by applying an etchant comprising a mixture of 12 gm I₂, 50 ml H₂ O, 8 gm KI, and 25 ml KOH (1 normal). This step self-aligns the contacts since etching occurs only over the gate, and also removes the possibility of source-to-gate-to-drain shorts in the final device.

It will be noted in FIG. 8 that if the step between gate oxide and field oxide is essentially vertical, some portion of the palladium layer, 16, may be shielded from reaction with the polycrystalline silicon, 19, at the step. This can be easily remedied by applying an etchant, which removes the unreacted palladium and thereby also removes the overlying portions of the insulator, 18, and polycrystalline silicon, 19. One such etchant is KI₃ in methanol with approximately 7 percent by weight KI, 2 percent by weight I₂, and the rest methanol. Any processing which smooths the field oxide to gate oxide steps over which layer, 16, is deposited will eliminate the need for a special undercut etch of any unreacted metal. For example, the selective oxidation process for growing field oxide produces a shallow gate oxide to field oxide slope. Layer, 15, could also be a spin-on glass which will also produce a smoother profile onto which the metal is deposited.

Next, as shown in FIG. 9, the As from the polycrystalline silicon, 19, may be diffused into the exposed semiconductor areas, 30 and 31, to form source and drain regions, 21 and 22, respectively. A typical heating step would be a temperature of approximately 950 degrees C. for approximately 30 min. It will be noted that the field oxide shields the semiconductor outside the transistor area from the diffusion. It will also be appreciated that the final junction depth of the source and drain regions will be established after all subsequent heat treatments.

The polycrystalline silicon layer, 19, may then be patterned into desired dimensions by standard photolithography as illustrated in the top view of FIG. 10. It will be noted that the final pattern of the polycrystalline silicon layer extends over the field oxide portions adjacent to the source and drain regions, and also seals the source and drain regions from contaminants. The polycrystalline silicon layer 19, may then be converted to a silicide layer (26 of FIG. 11) by depositing a metal, such as cobalt, and heating according to standard techniques. A typical heating step would be a temperature of 450 degrees C. for 30 min. in H₂, followed by 900 degrees C. for 30 min. in Ar with 2 percent O₂. The silicide layer would have the same geometry as the polycrystalline layer. If desired, the silicide layer could be formed prior to patterning the metal.

It will be appreciated that the use of silicide layer, 26, will lower series resistance between the contacts to source and drain regions and the channel since the layer, 26, is formed right up to the gate oxide, 13, and as close to the edges of the channel as possible. Although the entire polysilicon layer is converted to silicide in this example, it may also be desirable to so convert only a portion of the thickness of the layer so as to leave a multi-layer of polysilicon-silicide. In either case, the source and drain region vertical dimensions are not constricted by formation of silicide into the semiconductor. Further, the series resistance between source and drains and the channel can be optimized by controlling the relative thicknesses of the polysilicon and silicide layers without having to increase the source and drain junction depths.

In the final sequence of steps, as shown in FIG. 11, the device is covered by a layer, 23, such as phosphorus-doped glass, the surface is planarized, and windows, 32 and 33, are opened therein by standard photolithography to expose portions of the layer, 26. Contact is made to the source and drain through the silicide layer, 26, by depositing a contact metal such as aluminum, 24 and 25, in the windows. It will be noted that ohmic contact is made over the field oxide portions rather than directly over the source and drain regions. This feature provides several advantages. First, it permits the source and drain silicide contact areas, 30 and 31, to be made small (desirably, no greater than 0.5 μm) since the aluminum contact windows, 32 and 33, do not have to be aligned therewith. Second, it eliminates the problems of spiking between the aluminum and silicon substrate. Further, it also simplifies etching since the contacts, 24 and 25, to the source and drain are at approximately the same height as the contact to the gate electrode (not shown). This eliminates window growth (or "blooming") problems which can otherwise occur for windows to gate electrodes which are exposed to overetching while the windows to the source and drain are continuing to be etched. It will also be appreciated that a required overlapping of layer, 26, around the window is not necessary, since, even with a misalignment, there should be very little overetching required when all window depths are the same. It will also be noted that, although the metal contacts, 24 and 25, are shown overlapping the contact windows, 24 and 25, this overlap is also not necessary. Lay-out area can thereby be reduced. Finally, it may be noted that forming the contact over the field oxide reduces the depth of the windows, 32 and 33, and therefore improves the step converage of the A1 metal.

It will be realized that several modifications of the invention are possible. For example, the particular materials described are intended to be primarily illustrative and other materials which function in the same way may be substituted. All conductivity types shown may be reversed. Although an enhancement mode device has been illustrated, the invention is applicable to all types of field effect transistors. Although self-aligned removal of polysilicon above the gate is achieved in the above example by initially patterning a multi-level electrode structure, other methods might be employed. For example, a polysilicon gate could be defined in a standard manner and, subsequent to forming the sidewall oxide, a silicide-forming metal could be selectively plated or deposited by chemical vapor deposition over the gate electrode. The polysilicon layer, 19, could then be deposited and the silicide formed as before. Thus, in the attached claims, unless otherwise indicated, formation of a multi-level electrode structure including a silicide-forming metal need not be done sequentially before other recited steps. Useful silicide-forming metals, in addition to palladium, include nickel, tungsten, and tantalum.

Various additional modifications of the invention will become apparent to those skilled in the art. All such variations will basically rely on the teachings through which the invention has advanced the art are properly considered within the spirit and scope of the invention. 

What is claimed is:
 1. A method of fabricating a field effect transistor including a source and drain region formed in the surface of a semiconductor substrate with a channel region therebetween, the method comprising the steps of:forming over the channel region a multi-level electrode structure including successive layers of a gate electrode metal, a first insulator, and a silicide forming metal; forming a second insulator along the edges of the electrode structure; depositing a layer of polycrystalline silicon over essentially the entire transistor area; reacting the silicide forming metal with the polycrystalline silicon so as to form a metal silicide over the electrode structure; and selectively etching the metal silicide without affecting the first or second insulator or the remaining polycrystalline silicon layer.
 2. The method according to claim 1 further comprising the steps of converting at least a portion of the thickness of the remaining polycrystalline silicon layer into a second silicide layer and making ohmic contact thereto by forming a contact metal over a portion of said layer.
 3. The method according to claim 2 wherein the polycrystalline silicon layer is formed over a third insulating layer which includes thick and thin portions and ohmic contact is made to the resulting silicide layer over the thick portions of the insulator at an area removed from the source and drain regions.
 4. The method according to claim 3 wherein the polycrystalline silicon layer is only partially converted to silicide.
 5. The method according to claim 1 wherein the gate electrode metal comprises polycrystalline silicon, the first insulator comprises silicon dioxide, and the silicide forming metal comprises palladium.
 6. The method according to claim 3 wherein the ohmic contact is made to the silicide layer by a metal which comprises aluminum.
 7. The method according to claim 3 wherein the second silicide layer makes contact to the source and drain regions through openings in the thin portions of the third insulator which have a dimension in the direction of current conduction no greater than 0.5 μm.
 8. The method according to claim 1 wherein the second insulator is formed along the edges of the electrode structure by depositing a layer of silicon dioxide over the transistor and anisotropically etching the layer.
 9. The method according to claim 1 wherein the polycrystalline silicon layer includes impurities which are diffused into the semiconductor to form the source and drain regions.
 10. A method of fabricating a field effect transistor including a source and drain region formed in the surface of a semiconductor substrate with a channel region therebetween, the method comprisingforming over the substrate a first insulating layer which includes thick and thin portions, where the thin portions cover the area of the substrate which will comprise the transistor; successively forming over the channel region a multi-level electrode structure including successive layers of a first polycrystalline silicon, a first silicon dioxide, palladium, and a second silicon dioxide; following formation of the electrode structure, forming a third layer of silicon dioxide over the resulting structure, and anisotropically etching said layer to leave portions along the edges of the electrode, expose the palladium layer, and remove exposed areas of the thin portion of the first insulating layer; depositing a second layer of polycrystalline silicon doped with impurities having a conductivity type opposite to the substrate over essentially the entire transistor area; reacting the palladium layer with the polycrystalline layer to form palladium silicide over the electrode structure; selectively etching the palladium silicide without affecting the first silicon dioxide layer or the portions of silicon dioxide along the edges of the electrode structure or the remaining area of the second polycrystalline silicon layer; diffusing the impurities from the remaining second polycrystalline silicon layer into the areas of the substrate not covered by thin portions of the first insulator to form source and drain regions; converting the remaining second polycrystalline silicon layer into a second silicide layer; forming a second insulating layer over the resulting structure and exposing the second silicide layer over the thick portions of the first insulating layer in areas removed from the source and drain regions; and forming ohmic contact to the second silicide layer by depositing aluminum in the openings in the second insulating layer. 